BS ISO 36:2020 pdf free.Rubber vulcanized or thermoplastic-Determination of adhesion to textile fabrics.
BS ISO 36 1 Scope This document specifies a method of test for measuring the force required to separate, by stripping, two plies of fabric bonded with rubber, or a rubber layer and a fabric ply bonded together.The method is applicable when the ply surfaces are approximately plane or when they are in the form of a cylinder having an internal diameter greater than approximately 50 mm. The method is not applicable when the ply surfaces contain sharp bends, angles or other gross irregularities which cannot be excluded when cutting out test pieces. This document does not apply to coated fabrics, which are tested in accordance with ISO 2411 or textile
conveyor belts, which are tested in accordance with ISO 252. 2 Normative references The following documents are referred to in the text in such a way that some or all of their content constitutes requirements of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. ISO 5893:2019, Rubber and plastics test equipment- Tensile, flexural and compression types (constantrate of traverse)一Specification
ISO 6133:2015, Rubber and plastics一Analysis of multi-peak traces obtained in determinations of tearstrength and adhesion strength
ISO 18899:2013, Rubber – – . Guide to the calibration of test equipment ISO 23529, Rubber 一General procedures for preparing and conditioning test pieces for physicaltest methods.10 Conditioning of test pieces and temperature of test Condition all test pieces in accordance with ISO 23529. If the preparation of test pieces involves buffing, the interval between buffing and testing shall be not less than 16 h and not greater than 72 h. For tests at a standard laboratory temperature (see ISO 23529), test pieces that do not require further preparation may be tested immediately, if cut from conditioned test samples. Where additional preparation is involved, a minimum conditioning period of 3 h at a standard laboratory temperature shall be allowed. For tests at temperatures other than a standard laboratory temperature, condition the test pieces at the temperature at which the test is to be conducted for a period sufficient to enable the test pieces to attain substantial equilibrium in accordance with ISO 23529.BS ISO 36 pdf download.